90-silver 10-tin-oxide vs. ISO-WD32250 Magnesium
90-silver 10-tin-oxide belongs to the otherwise unclassified metals classification, while ISO-WD32250 magnesium belongs to the magnesium alloys. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-tin-oxide and the bottom bar is ISO-WD32250 magnesium.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 77 to 82 | |
| 25 |
| Elongation at Break, % | 7.0 to 35 | |
| 4.5 to 8.6 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 68 | |
| 14 to 26 |
| Shear Strength, MPa | 160 to 170 | |
| 180 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 300 | |
| 310 to 330 |
| Tensile Strength: Yield (Proof), MPa | 120 to 280 | |
| 240 to 290 |