90-silver 10-tin-oxide vs. ZK60A Magnesium
90-silver 10-tin-oxide belongs to the otherwise unclassified metals classification, while ZK60A magnesium belongs to the magnesium alloys. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is 90-silver 10-tin-oxide and the bottom bar is ZK60A magnesium.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 77 to 82 | |
| 29 to 30 |
| Elongation at Break, % | 7.0 to 35 | |
| 4.5 to 9.9 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 20 to 68 | |
| 14 to 29 |
| Shear Strength, MPa | 160 to 170 | |
| 170 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 300 | |
| 320 to 330 |
| Tensile Strength: Yield (Proof), MPa | 120 to 280 | |
| 230 to 250 |