92-silver 8-tin-oxide vs. ASTM A414 Steel
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while ASTM A414 steel belongs to the iron alloys. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is ASTM A414 steel.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 76 to 80 | |
| 7.2 to 7.3 |
| Elongation at Break, % | 32 to 34 | |
| 15 to 26 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 69 to 130 |
| Shear Strength, MPa | 150 to 210 | |
| 230 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 360 to 590 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 190 to 350 |