92-silver 8-tin-oxide vs. ISO-WD21150 Magnesium
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while ISO-WD21150 magnesium belongs to the magnesium alloys. There are 6 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is ISO-WD21150 magnesium.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 76 to 80 | |
| 19 |
| Elongation at Break, % | 32 to 34 | |
| 5.7 to 11 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 15 to 24 |
| Shear Strength, MPa | 150 to 210 | |
| 150 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 240 to 290 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 120 to 200 |