A242.0 Aluminum vs. 2007 Aluminum

Both A242.0 aluminum and 2007 aluminum are aluminum alloys. They have a very high 97% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is A242.0 aluminum and the bottom bar is 2007 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 73
71
Elongation at Break, % 1.6
5.6 to 8.0
Poisson's Ratio 0.33
0.33
Shear Modulus, GPa 27
27
Tensile Strength: Ultimate (UTS), MPa 220
370 to 420

Thermal Properties

Latent Heat of Fusion, J/g 390
390
Maximum Temperature: Mechanical, °C 210
190
Melting Completion (Liquidus), °C 680
640
Melting Onset (Solidus), °C 550
510
Specific Heat Capacity, J/kg-K 870
870
Thermal Conductivity, W/m-K 140
130
Thermal Expansion, µm/m-K 23
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 37
47
Electrical Conductivity: Equal Weight (Specific), % IACS 110
140

Otherwise Unclassified Properties

Base Metal Price, % relative 12
11
Density, g/cm3 3.1
3.1
Embodied Carbon, kg CO2/kg material 8.3
8.0
Embodied Energy, MJ/kg 150
150
Embodied Water, L/kg 1130
1130

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 45
44
Strength to Weight: Axial, points 20
33 to 38
Strength to Weight: Bending, points 26
37 to 40
Thermal Diffusivity, mm2/s 52
48
Thermal Shock Resistance, points 9.3
16 to 19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 89.3 to 93.1
87.5 to 95
Bismuth (Bi), % 0
0 to 0.2
Chromium (Cr), % 0.15 to 0.25
0 to 0.1
Copper (Cu), % 3.7 to 4.5
3.3 to 4.6
Iron (Fe), % 0 to 0.8
0 to 0.8
Lead (Pb), % 0
0.8 to 1.5
Magnesium (Mg), % 1.2 to 1.7
0.4 to 1.8
Manganese (Mn), % 0 to 0.1
0.5 to 1.0
Nickel (Ni), % 1.8 to 2.3
0 to 0.2
Silicon (Si), % 0 to 0.6
0 to 0.8
Tin (Sn), % 0
0 to 0.2
Titanium (Ti), % 0.070 to 0.2
0 to 0.2
Zinc (Zn), % 0 to 0.1
0 to 0.8
Residuals, % 0 to 0.15
0 to 0.3