ACI-ASTM CA15M Steel vs. ASTM A202 Steel

Both ACI-ASTM CA15M steel and ASTM A202 steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA15M steel and the bottom bar is ASTM A202 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
180 to 200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 20
17 to 18
Fatigue Strength, MPa 330
240
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 690
590 to 670
Tensile Strength: Yield (Proof), MPa 510
350 to 360

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Maximum Temperature: Mechanical, °C 760
410
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 27
52
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.5
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.1
1.4
Embodied Energy, MJ/kg 29
19
Embodied Water, L/kg 100
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
93 to 96
Resilience: Unit (Modulus of Resilience), kJ/m3 670
330 to 350
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25
21 to 24
Strength to Weight: Bending, points 22
20 to 22
Thermal Diffusivity, mm2/s 7.2
14
Thermal Shock Resistance, points 25
17 to 20