ACI-ASTM CA28MWV Steel vs. ASTM A204 Steel

Both ACI-ASTM CA28MWV steel and ASTM A204 steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA28MWV steel and the bottom bar is ASTM A204 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
160 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11
18 to 22
Fatigue Strength, MPa 470
200 to 220
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 1080
520 to 590
Tensile Strength: Yield (Proof), MPa 870
290 to 330

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 740
410
Melting Completion (Liquidus), °C 1470
1470
Melting Onset (Solidus), °C 1430
1420 to 1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 25
52
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.6
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 11
2.4
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 3.1
1.5
Embodied Energy, MJ/kg 44
20
Embodied Water, L/kg 100
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
90 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 1920
220 to 290
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 38
18 to 21
Strength to Weight: Bending, points 30
18 to 20
Thermal Diffusivity, mm2/s 6.6
14
Thermal Shock Resistance, points 40
15 to 17