ACI-ASTM CA28MWV Steel vs. AWS E209

Both ACI-ASTM CA28MWV steel and AWS E209 are iron alloys. They have 73% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA28MWV steel and the bottom bar is AWS E209.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 11
17
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 1080
770

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Melting Completion (Liquidus), °C 1470
1420
Melting Onset (Solidus), °C 1430
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 10
14

Otherwise Unclassified Properties

Base Metal Price, % relative 11
21
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.1
4.4
Embodied Energy, MJ/kg 44
63
Embodied Water, L/kg 100
180

Common Calculations

PREN (Pitting Resistance) 17
33
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 38
28
Strength to Weight: Bending, points 30
24
Thermal Shock Resistance, points 40
19

Alloy Composition

Carbon (C), % 0.2 to 0.28
0 to 0.060
Chromium (Cr), % 11 to 12.5
20.5 to 24
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 81.4 to 85.8
51.5 to 64.3
Manganese (Mn), % 0.5 to 1.0
4.0 to 7.0
Molybdenum (Mo), % 0.9 to 1.3
1.5 to 3.0
Nickel (Ni), % 0.5 to 1.0
9.5 to 12
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.9 to 1.3
0
Vanadium (V), % 0.2 to 0.3
0.1 to 0.3