ACI-ASTM CA28MWV Steel vs. EN 1.3555 Steel

Both ACI-ASTM CA28MWV steel and EN 1.3555 steel are iron alloys. They have a moderately high 90% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA28MWV steel and the bottom bar is EN 1.3555 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
230
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
75
Tensile Strength: Ultimate (UTS), MPa 1080
770

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Maximum Temperature: Mechanical, °C 740
540
Melting Completion (Liquidus), °C 1470
1500
Melting Onset (Solidus), °C 1430
1450
Specific Heat Capacity, J/kg-K 470
460
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.6
9.3
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
11

Otherwise Unclassified Properties

Base Metal Price, % relative 11
11
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 3.1
5.6
Embodied Energy, MJ/kg 44
81
Embodied Water, L/kg 100
90

Common Calculations

PREN (Pitting Resistance) 17
18
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 38
27
Strength to Weight: Bending, points 30
23
Thermal Shock Resistance, points 40
22

Alloy Composition

Carbon (C), % 0.2 to 0.28
0.1 to 0.15
Chromium (Cr), % 11 to 12.5
3.9 to 4.3
Copper (Cu), % 0
0 to 0.1
Iron (Fe), % 81.4 to 85.8
85.4 to 87.7
Manganese (Mn), % 0.5 to 1.0
0.15 to 0.35
Molybdenum (Mo), % 0.9 to 1.3
4.0 to 4.5
Nickel (Ni), % 0.5 to 1.0
3.2 to 3.6
Phosphorus (P), % 0 to 0.030
0 to 0.015
Silicon (Si), % 0 to 1.0
0.1 to 0.25
Sulfur (S), % 0 to 0.030
0 to 0.010
Tungsten (W), % 0.9 to 1.3
0 to 0.15
Vanadium (V), % 0.2 to 0.3
1.0 to 1.3