ACI-ASTM CA28MWV Steel vs. EN 1.4309 Stainless Steel

Both ACI-ASTM CA28MWV steel and EN 1.4309 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA28MWV steel and the bottom bar is EN 1.4309 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
140
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 11
34
Fatigue Strength, MPa 470
170
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 1080
490
Tensile Strength: Yield (Proof), MPa 870
210

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Corrosion, °C 380
420
Maximum Temperature: Mechanical, °C 740
960
Melting Completion (Liquidus), °C 1470
1420
Melting Onset (Solidus), °C 1430
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 25
15
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.6
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 11
16
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.1
3.1
Embodied Energy, MJ/kg 44
45
Embodied Water, L/kg 100
150

Common Calculations

PREN (Pitting Resistance) 17
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
140
Resilience: Unit (Modulus of Resilience), kJ/m3 1920
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 38
18
Strength to Weight: Bending, points 30
18
Thermal Diffusivity, mm2/s 6.6
4.1
Thermal Shock Resistance, points 40
11

Alloy Composition

Carbon (C), % 0.2 to 0.28
0 to 0.030
Chromium (Cr), % 11 to 12.5
18 to 20
Iron (Fe), % 81.4 to 85.8
64.2 to 73
Manganese (Mn), % 0.5 to 1.0
0 to 2.0
Molybdenum (Mo), % 0.9 to 1.3
0
Nickel (Ni), % 0.5 to 1.0
9.0 to 12
Nitrogen (N), % 0
0 to 0.2
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.025
Tungsten (W), % 0.9 to 1.3
0
Vanadium (V), % 0.2 to 0.3
0