ACI-ASTM CA28MWV Steel vs. EN 1.8152 Steel

Both ACI-ASTM CA28MWV steel and EN 1.8152 steel are iron alloys. They have 86% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA28MWV steel and the bottom bar is EN 1.8152 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
200 to 540
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 1080
660 to 2010

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Maximum Temperature: Mechanical, °C 740
410
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 25
47
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.6
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 11
2.2
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 3.1
1.8
Embodied Energy, MJ/kg 44
25
Embodied Water, L/kg 100
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 38
24 to 72
Strength to Weight: Bending, points 30
22 to 46
Thermal Diffusivity, mm2/s 6.6
13
Thermal Shock Resistance, points 40
20 to 60

Alloy Composition

Carbon (C), % 0.2 to 0.28
0.51 to 0.59
Chromium (Cr), % 11 to 12.5
0.5 to 0.8
Iron (Fe), % 81.4 to 85.8
96 to 97.2
Manganese (Mn), % 0.5 to 1.0
0.5 to 0.8
Molybdenum (Mo), % 0.9 to 1.3
0
Nickel (Ni), % 0.5 to 1.0
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 1.0
1.2 to 1.6
Sulfur (S), % 0 to 0.030
0 to 0.025
Tungsten (W), % 0.9 to 1.3
0
Vanadium (V), % 0.2 to 0.3
0.1 to 0.2