ACI-ASTM CA28MWV Steel vs. EN 1.8527 Steel

Both ACI-ASTM CA28MWV steel and EN 1.8527 steel are iron alloys. They have 89% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA28MWV steel and the bottom bar is EN 1.8527 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
270
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11
16
Fatigue Strength, MPa 470
520
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
74
Tensile Strength: Ultimate (UTS), MPa 1080
900
Tensile Strength: Yield (Proof), MPa 870
800

Thermal Properties

Latent Heat of Fusion, J/g 270
260
Maximum Temperature: Mechanical, °C 740
490
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 25
41
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.6
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 11
4.0
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.7
Embodied Energy, MJ/kg 44
23
Embodied Water, L/kg 100
66

Common Calculations

PREN (Pitting Resistance) 17
5.7
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
140
Resilience: Unit (Modulus of Resilience), kJ/m3 1920
1670
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 38
32
Strength to Weight: Bending, points 30
26
Thermal Diffusivity, mm2/s 6.6
11
Thermal Shock Resistance, points 40
26

Alloy Composition

Carbon (C), % 0.2 to 0.28
0.040 to 0.12
Chromium (Cr), % 11 to 12.5
3.7 to 4.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 81.4 to 85.8
93.2 to 95.1
Manganese (Mn), % 0.5 to 1.0
0.85 to 1.2
Molybdenum (Mo), % 0.9 to 1.3
0.4 to 0.6
Nickel (Ni), % 0.5 to 1.0
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.035
Tungsten (W), % 0.9 to 1.3
0
Vanadium (V), % 0.2 to 0.3
0