ACI-ASTM CA28MWV Steel vs. EN 1.8837 Steel

Both ACI-ASTM CA28MWV steel and EN 1.8837 steel are iron alloys. They have 85% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA28MWV steel and the bottom bar is EN 1.8837 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11
19
Fatigue Strength, MPa 470
340
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 1080
630
Tensile Strength: Yield (Proof), MPa 870
490

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 740
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 25
49
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.6
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 11
2.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.6
Embodied Energy, MJ/kg 44
21
Embodied Water, L/kg 100
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
110
Resilience: Unit (Modulus of Resilience), kJ/m3 1920
640
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 38
22
Strength to Weight: Bending, points 30
21
Thermal Diffusivity, mm2/s 6.6
13
Thermal Shock Resistance, points 40
18

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.040
Carbon (C), % 0.2 to 0.28
0 to 0.16
Chromium (Cr), % 11 to 12.5
0
Iron (Fe), % 81.4 to 85.8
96.6 to 99.98
Manganese (Mn), % 0.5 to 1.0
0 to 1.7
Molybdenum (Mo), % 0.9 to 1.3
0 to 0.2
Nickel (Ni), % 0.5 to 1.0
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.0050
Titanium (Ti), % 0
0 to 0.050
Tungsten (W), % 0.9 to 1.3
0
Vanadium (V), % 0.2 to 0.3
0 to 0.1