ACI-ASTM CA28MWV Steel vs. Grade 300 Maraging Steel

Both ACI-ASTM CA28MWV steel and grade 300 maraging steel are iron alloys. They have 69% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA28MWV steel and the bottom bar is grade 300 maraging steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11
6.5 to 18
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 76
75
Tensile Strength: Ultimate (UTS), MPa 1080
1030 to 2030
Tensile Strength: Yield (Proof), MPa 870
760 to 1990

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Melting Completion (Liquidus), °C 1470
1480
Melting Onset (Solidus), °C 1430
1430
Specific Heat Capacity, J/kg-K 470
450
Thermal Expansion, µm/m-K 10
12

Otherwise Unclassified Properties

Base Metal Price, % relative 11
34
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 3.1
5.1
Embodied Energy, MJ/kg 44
68
Embodied Water, L/kg 100
150

Common Calculations

PREN (Pitting Resistance) 17
16
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
130 to 170
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 38
35 to 68
Strength to Weight: Bending, points 30
28 to 43
Thermal Shock Resistance, points 40
31 to 62

Alloy Composition

Aluminum (Al), % 0
0.050 to 0.15
Boron (B), % 0
0 to 0.0030
Calcium (Ca), % 0
0 to 0.050
Carbon (C), % 0.2 to 0.28
0 to 0.030
Chromium (Cr), % 11 to 12.5
0
Cobalt (Co), % 0
8.5 to 9.5
Iron (Fe), % 81.4 to 85.8
65 to 68.4
Manganese (Mn), % 0.5 to 1.0
0 to 0.1
Molybdenum (Mo), % 0.9 to 1.3
4.6 to 5.2
Nickel (Ni), % 0.5 to 1.0
18 to 19
Phosphorus (P), % 0 to 0.030
0 to 0.010
Silicon (Si), % 0 to 1.0
0 to 0.1
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0.5 to 0.8
Tungsten (W), % 0.9 to 1.3
0
Vanadium (V), % 0.2 to 0.3
0
Zirconium (Zr), % 0
0 to 0.020