ACI-ASTM CA28MWV Steel vs. SAE-AISI 1010 Steel

Both ACI-ASTM CA28MWV steel and SAE-AISI 1010 steel are iron alloys. They have 84% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA28MWV steel and the bottom bar is SAE-AISI 1010 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 330
100 to 110
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11
22 to 31
Fatigue Strength, MPa 470
150 to 230
Poisson's Ratio 0.28
0.29
Reduction in Area, % 27
46 to 56
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 1080
350 to 400
Tensile Strength: Yield (Proof), MPa 870
190 to 330

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 740
400
Melting Completion (Liquidus), °C 1470
1470
Melting Onset (Solidus), °C 1430
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 25
47
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 4.6
12
Electrical Conductivity: Equal Weight (Specific), % IACS 5.3
14

Otherwise Unclassified Properties

Base Metal Price, % relative 11
1.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 3.1
1.4
Embodied Energy, MJ/kg 44
18
Embodied Water, L/kg 100
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
82 to 93
Resilience: Unit (Modulus of Resilience), kJ/m3 1920
100 to 290
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 38
12 to 14
Strength to Weight: Bending, points 30
14 to 15
Thermal Diffusivity, mm2/s 6.6
13
Thermal Shock Resistance, points 40
11 to 13

Alloy Composition

Carbon (C), % 0.2 to 0.28
0.080 to 0.13
Chromium (Cr), % 11 to 12.5
0
Iron (Fe), % 81.4 to 85.8
99.18 to 99.62
Manganese (Mn), % 0.5 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 0.9 to 1.3
0
Nickel (Ni), % 0.5 to 1.0
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050
Tungsten (W), % 0.9 to 1.3
0
Vanadium (V), % 0.2 to 0.3
0