ACI-ASTM CB30 Steel vs. ASTM A283 Carbon Steel

Both ACI-ASTM CB30 steel and ASTM A283 carbon steel are iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB30 steel and the bottom bar is ASTM A283 carbon steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
110 to 140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 500
360 to 480
Tensile Strength: Yield (Proof), MPa 230
180 to 260

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 940
400
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 21
51 to 53
Thermal Expansion, µm/m-K 11
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 10
1.8
Density, g/cm3 7.7
7.8 to 7.9
Embodied Carbon, kg CO2/kg material 2.3
1.4
Embodied Energy, MJ/kg 33
18
Embodied Water, L/kg 130
46

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 140
91 to 180
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
13 to 17
Strength to Weight: Bending, points 18
14 to 17
Thermal Diffusivity, mm2/s 5.6
14
Thermal Shock Resistance, points 17
11 to 15