ACI-ASTM CB30 Steel vs. C46200 Brass
ACI-ASTM CB30 steel belongs to the iron alloys classification, while C46200 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CB30 steel and the bottom bar is C46200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 100 |
| Poisson's Ratio | 0.28 | |
| 0.31 |
| Shear Modulus, GPa | 77 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 500 | |
| 370 to 480 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 120 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 940 | |
| 120 |
| Melting Completion (Liquidus), °C | 1430 | |
| 840 |
| Melting Onset (Solidus), °C | 1380 | |
| 800 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 380 |
| Thermal Conductivity, W/m-K | 21 | |
| 110 |
| Thermal Expansion, µm/m-K | 11 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 24 |
| Density, g/cm3 | 7.7 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 2.3 | |
| 2.7 |
| Embodied Energy, MJ/kg | 33 | |
| 46 |
| Embodied Water, L/kg | 130 | |
| 330 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
| 72 to 400 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 18 | |
| 13 to 16 |
| Strength to Weight: Bending, points | 18 | |
| 14 to 17 |
| Thermal Diffusivity, mm2/s | 5.6 | |
| 35 |
| Thermal Shock Resistance, points | 17 | |
| 12 to 16 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.3 | |
| 0 |
| Chromium (Cr), % | 18 to 21 | |
| 0 |
| Copper (Cu), % | 0 to 1.2 | |
| 62 to 65 |
| Iron (Fe), % | 72.9 to 82 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Nickel (Ni), % | 0 to 2.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.5 to 1.0 |
| Zinc (Zn), % | 0 | |
| 33.3 to 37.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |