ACI-ASTM CB30 Steel vs. R30021 Cobalt

ACI-ASTM CB30 steel belongs to the iron alloys classification, while R30021 cobalt belongs to the cobalt alloys. They have a modest 23% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB30 steel and the bottom bar is R30021 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
220
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
86
Tensile Strength: Ultimate (UTS), MPa 500
700
Tensile Strength: Yield (Proof), MPa 230
500

Thermal Properties

Latent Heat of Fusion, J/g 290
330
Melting Completion (Liquidus), °C 1430
1350
Melting Onset (Solidus), °C 1380
1190
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 21
15
Thermal Expansion, µm/m-K 11
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
2.1

Otherwise Unclassified Properties

Density, g/cm3 7.7
8.4
Embodied Carbon, kg CO2/kg material 2.3
8.0
Embodied Energy, MJ/kg 33
110
Embodied Water, L/kg 130
520

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 140
570
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
23
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 5.6
3.8
Thermal Shock Resistance, points 17
21

Alloy Composition

Carbon (C), % 0 to 0.3
0.2 to 0.35
Chromium (Cr), % 18 to 21
26 to 29
Cobalt (Co), % 0
61.7 to 67.3
Copper (Cu), % 0 to 1.2
0
Iron (Fe), % 72.9 to 82
0 to 3.0
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 0
4.5 to 6.0
Nickel (Ni), % 0 to 2.0
2.0 to 3.0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.5
0 to 1.5
Sulfur (S), % 0 to 0.040
0