ACI-ASTM CB6 Steel vs. AISI 305 Stainless Steel

Both ACI-ASTM CB6 steel and AISI 305 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB6 steel and the bottom bar is AISI 305 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 18
34 to 45
Fatigue Strength, MPa 410
210 to 280
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 880
580 to 710
Tensile Strength: Yield (Proof), MPa 660
230 to 350

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 870
540
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
16
Thermal Expansion, µm/m-K 10
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
16
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.5
3.2
Embodied Energy, MJ/kg 36
45
Embodied Water, L/kg 130
150

Common Calculations

PREN (Pitting Resistance) 17
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
200 to 210
Resilience: Unit (Modulus of Resilience), kJ/m3 1110
130 to 320
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 32
20 to 25
Strength to Weight: Bending, points 26
20 to 23
Thermal Diffusivity, mm2/s 4.6
4.2
Thermal Shock Resistance, points 31
13 to 15

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.12
Chromium (Cr), % 15.5 to 17.5
17 to 19
Iron (Fe), % 74.4 to 81
65.1 to 72.5
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 3.5 to 5.5
10.5 to 13
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030