ACI-ASTM CB6 Steel vs. AISI 317LN Stainless Steel

Both ACI-ASTM CB6 steel and AISI 317LN stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB6 steel and the bottom bar is AISI 317LN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 18
45
Fatigue Strength, MPa 410
250
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
79
Tensile Strength: Ultimate (UTS), MPa 880
620
Tensile Strength: Yield (Proof), MPa 660
270

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 410
420
Maximum Temperature: Mechanical, °C 870
1010
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
14
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
21
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.5
4.3
Embodied Energy, MJ/kg 36
59
Embodied Water, L/kg 130
160

Common Calculations

PREN (Pitting Resistance) 17
33
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
220
Resilience: Unit (Modulus of Resilience), kJ/m3 1110
190
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 32
22
Strength to Weight: Bending, points 26
20
Thermal Diffusivity, mm2/s 4.6
3.9
Thermal Shock Resistance, points 31
14

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.030
Chromium (Cr), % 15.5 to 17.5
18 to 20
Iron (Fe), % 74.4 to 81
57.9 to 67.9
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
3.0 to 4.0
Nickel (Ni), % 3.5 to 5.5
11 to 15
Nitrogen (N), % 0
0.1 to 0.22
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030