ACI-ASTM CB6 Steel vs. ASTM A182 Grade F2

Both ACI-ASTM CB6 steel and ASTM A182 grade F2 are iron alloys. They have 80% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB6 steel and the bottom bar is ASTM A182 grade F2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 18
23
Fatigue Strength, MPa 410
220
Poisson's Ratio 0.28
0.29
Reduction in Area, % 40
34
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 880
550
Tensile Strength: Yield (Proof), MPa 660
310

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
420
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
46
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.7
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.5
1.6
Embodied Energy, MJ/kg 36
21
Embodied Water, L/kg 130
50

Common Calculations

PREN (Pitting Resistance) 17
2.5
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
110
Resilience: Unit (Modulus of Resilience), kJ/m3 1110
250
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 32
20
Strength to Weight: Bending, points 26
19
Thermal Diffusivity, mm2/s 4.6
12
Thermal Shock Resistance, points 31
16

Alloy Composition

Carbon (C), % 0 to 0.060
0.050 to 0.21
Chromium (Cr), % 15.5 to 17.5
0.5 to 0.81
Iron (Fe), % 74.4 to 81
96.9 to 98.6
Manganese (Mn), % 0 to 1.0
0.3 to 0.8
Molybdenum (Mo), % 0 to 0.5
0.44 to 0.65
Nickel (Ni), % 3.5 to 5.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0.1 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.040