ACI-ASTM CB6 Steel vs. EN 1.0213 Steel

Both ACI-ASTM CB6 steel and EN 1.0213 steel are iron alloys. They have 78% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB6 steel and the bottom bar is EN 1.0213 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 18
12 to 25
Fatigue Strength, MPa 410
160 to 240
Poisson's Ratio 0.28
0.29
Reduction in Area, % 40
72 to 80
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 880
320 to 430
Tensile Strength: Yield (Proof), MPa 660
220 to 330

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
400
Melting Completion (Liquidus), °C 1440
1470
Melting Onset (Solidus), °C 1390
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
53
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.5
1.4
Embodied Energy, MJ/kg 36
18
Embodied Water, L/kg 130
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
33 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 1110
120 to 300
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 32
11 to 15
Strength to Weight: Bending, points 26
13 to 16
Thermal Diffusivity, mm2/s 4.6
14
Thermal Shock Resistance, points 31
10 to 14

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.060
0.060 to 0.1
Chromium (Cr), % 15.5 to 17.5
0
Iron (Fe), % 74.4 to 81
99.245 to 99.67
Manganese (Mn), % 0 to 1.0
0.25 to 0.45
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 3.5 to 5.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.1
Sulfur (S), % 0 to 0.030
0 to 0.025