ACI-ASTM CB6 Steel vs. EN 1.3519 Steel

Both ACI-ASTM CB6 steel and EN 1.3519 steel are iron alloys. They have 80% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB6 steel and the bottom bar is EN 1.3519 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
72
Tensile Strength: Ultimate (UTS), MPa 880
620 to 730

Thermal Properties

Latent Heat of Fusion, J/g 280
260
Maximum Temperature: Mechanical, °C 870
430
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
43
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.5
1.5
Embodied Energy, MJ/kg 36
21
Embodied Water, L/kg 130
55

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 32
22 to 26
Strength to Weight: Bending, points 26
21 to 23
Thermal Diffusivity, mm2/s 4.6
12
Thermal Shock Resistance, points 31
18 to 22

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.060
0.93 to 1.1
Chromium (Cr), % 15.5 to 17.5
1.4 to 1.7
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 74.4 to 81
95.4 to 96.8
Manganese (Mn), % 0 to 1.0
1.4 to 1.7
Molybdenum (Mo), % 0 to 0.5
0 to 0.1
Nickel (Ni), % 3.5 to 5.5
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0.45 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030