ACI-ASTM CB6 Steel vs. EN 1.3536 Steel

Both ACI-ASTM CB6 steel and EN 1.3536 steel are iron alloys. They have 81% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB6 steel and the bottom bar is EN 1.3536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 880
660

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
440
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
41
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.5
1.6
Embodied Energy, MJ/kg 36
21
Embodied Water, L/kg 130
55

Common Calculations

PREN (Pitting Resistance) 17
2.8
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 32
23
Strength to Weight: Bending, points 26
22
Thermal Diffusivity, mm2/s 4.6
11
Thermal Shock Resistance, points 31
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.060
0.93 to 1.1
Chromium (Cr), % 15.5 to 17.5
1.7 to 2.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 74.4 to 81
96 to 97.4
Manganese (Mn), % 0 to 1.0
0.6 to 0.8
Molybdenum (Mo), % 0 to 0.5
0.2 to 0.35
Nickel (Ni), % 3.5 to 5.5
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0.15 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.030