ACI-ASTM CB6 Steel vs. EN 1.4854 Stainless Steel

Both ACI-ASTM CB6 steel and EN 1.4854 stainless steel are iron alloys. They have 59% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB6 steel and the bottom bar is EN 1.4854 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 18
45
Fatigue Strength, MPa 410
310
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Tensile Strength: Ultimate (UTS), MPa 880
750
Tensile Strength: Yield (Proof), MPa 660
340

Thermal Properties

Latent Heat of Fusion, J/g 280
330
Maximum Temperature: Corrosion, °C 410
450
Maximum Temperature: Mechanical, °C 870
1170
Melting Completion (Liquidus), °C 1440
1370
Melting Onset (Solidus), °C 1390
1330
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
11
Thermal Expansion, µm/m-K 10
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 12
34
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.5
5.7
Embodied Energy, MJ/kg 36
81
Embodied Water, L/kg 130
220

Common Calculations

PREN (Pitting Resistance) 17
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
270
Resilience: Unit (Modulus of Resilience), kJ/m3 1110
280
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 32
26
Strength to Weight: Bending, points 26
23
Thermal Diffusivity, mm2/s 4.6
2.9
Thermal Shock Resistance, points 31
18

Alloy Composition

Carbon (C), % 0 to 0.060
0.040 to 0.080
Cerium (Ce), % 0
0.030 to 0.080
Chromium (Cr), % 15.5 to 17.5
24 to 26
Iron (Fe), % 74.4 to 81
33.6 to 40.6
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 3.5 to 5.5
34 to 36
Nitrogen (N), % 0
0.12 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
1.2 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.015