ACI-ASTM CB6 Steel vs. EN 1.6571 Steel

Both ACI-ASTM CB6 steel and EN 1.6571 steel are iron alloys. They have 81% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB6 steel and the bottom bar is EN 1.6571 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 880
520 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
420
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
40
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 12
3.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.5
1.7
Embodied Energy, MJ/kg 36
22
Embodied Water, L/kg 130
53

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 32
19 to 51
Strength to Weight: Bending, points 26
18 to 36
Thermal Diffusivity, mm2/s 4.6
11
Thermal Shock Resistance, points 31
15 to 43

Alloy Composition

Carbon (C), % 0 to 0.060
0.16 to 0.23
Chromium (Cr), % 15.5 to 17.5
0.6 to 0.9
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 74.4 to 81
95.3 to 97.1
Manganese (Mn), % 0 to 1.0
0.5 to 0.9
Molybdenum (Mo), % 0 to 0.5
0.25 to 0.35
Nickel (Ni), % 3.5 to 5.5
1.4 to 1.7
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.030
0.020 to 0.040