ACI-ASTM CB6 Steel vs. Grade VDCrV Steel

Both ACI-ASTM CB6 steel and grade VDCrV steel are iron alloys. They have 79% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB6 steel and the bottom bar is grade VDCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Reduction in Area, % 40
51
Shear Modulus, GPa 77
80
Tensile Strength: Ultimate (UTS), MPa 880
1730

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
410
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
49
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.5
1.9
Embodied Energy, MJ/kg 36
26
Embodied Water, L/kg 130
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 32
61
Strength to Weight: Bending, points 26
41
Thermal Diffusivity, mm2/s 4.6
13
Thermal Shock Resistance, points 31
51

Alloy Composition

Carbon (C), % 0 to 0.060
0.62 to 0.72
Chromium (Cr), % 15.5 to 17.5
0.4 to 0.6
Copper (Cu), % 0
0 to 0.060
Iron (Fe), % 74.4 to 81
97.8 to 98.8
Manganese (Mn), % 0 to 1.0
0.5 to 0.9
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 3.5 to 5.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0.15 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.020
Vanadium (V), % 0
0.15 to 0.25