ACI-ASTM CB6 Steel vs. SAE-AISI 1035 Steel

Both ACI-ASTM CB6 steel and SAE-AISI 1035 steel are iron alloys. They have 78% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB6 steel and the bottom bar is SAE-AISI 1035 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 18
13 to 21
Fatigue Strength, MPa 410
210 to 340
Poisson's Ratio 0.28
0.29
Reduction in Area, % 40
40 to 45
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 880
570 to 620
Tensile Strength: Yield (Proof), MPa 660
300 to 530

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
51
Thermal Expansion, µm/m-K 10
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 12
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.5
1.4
Embodied Energy, MJ/kg 36
18
Embodied Water, L/kg 130
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
79 to 99
Resilience: Unit (Modulus of Resilience), kJ/m3 1110
250 to 740
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 32
20 to 22
Strength to Weight: Bending, points 26
19 to 21
Thermal Diffusivity, mm2/s 4.6
14
Thermal Shock Resistance, points 31
18 to 20

Alloy Composition

Carbon (C), % 0 to 0.060
0.32 to 0.38
Chromium (Cr), % 15.5 to 17.5
0
Iron (Fe), % 74.4 to 81
98.6 to 99.08
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 3.5 to 5.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050