ACI-ASTM CB7Cu-1 Steel vs. C61900 Bronze
ACI-ASTM CB7Cu-1 steel belongs to the iron alloys classification, while C61900 bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CB7Cu-1 steel and the bottom bar is C61900 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 5.7 to 11 | |
| 21 to 32 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 76 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 960 to 1350 | |
| 570 to 650 |
| Tensile Strength: Yield (Proof), MPa | 760 to 1180 | |
| 230 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 230 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1050 |
| Melting Onset (Solidus), °C | 1500 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 440 |
| Thermal Conductivity, W/m-K | 17 | |
| 79 |
| Thermal Expansion, µm/m-K | 11 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.3 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 28 |
| Density, g/cm3 | 7.8 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 3.1 |
| Embodied Energy, MJ/kg | 38 | |
| 51 |
| Embodied Water, L/kg | 130 | |
| 380 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 71 to 120 | |
| 110 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1500 to 3590 | |
| 230 to 430 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 34 to 48 | |
| 19 to 22 |
| Strength to Weight: Bending, points | 28 to 35 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 4.6 | |
| 22 |
| Thermal Shock Resistance, points | 32 to 45 | |
| 20 to 23 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 | |
| 8.5 to 10 |
| Carbon (C), % | 0 to 0.070 | |
| 0 |
| Chromium (Cr), % | 15.5 to 17.7 | |
| 0 |
| Copper (Cu), % | 2.5 to 3.2 | |
| 83.6 to 88.5 |
| Iron (Fe), % | 72.3 to 78.4 | |
| 3.0 to 4.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0 to 0.7 | |
| 0 |
| Nickel (Ni), % | 3.6 to 4.6 | |
| 0 |
| Niobium (Nb), % | 0 to 0.35 | |
| 0 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.6 |
| Zinc (Zn), % | 0 | |
| 0 to 0.8 |
| Residuals, % | 0 | |
| 0 to 0.5 |