ACI-ASTM CB7Cu-1 Steel vs. R30003 Cobalt
ACI-ASTM CB7Cu-1 steel belongs to the iron alloys classification, while R30003 cobalt belongs to the cobalt alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CB7Cu-1 steel and the bottom bar is R30003 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 5.7 to 11 | |
| 10 to 73 |
| Fatigue Strength, MPa | 420 to 590 | |
| 320 to 560 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 960 to 1350 | |
| 970 to 1720 |
| Tensile Strength: Yield (Proof), MPa | 760 to 1180 | |
| 510 to 1090 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 310 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1400 |
| Melting Onset (Solidus), °C | 1500 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Conductivity, W/m-K | 17 | |
| 13 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.3 | |
| 2.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 95 |
| Density, g/cm3 | 7.8 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 8.0 |
| Embodied Energy, MJ/kg | 38 | |
| 110 |
| Embodied Water, L/kg | 130 | |
| 400 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1500 to 3590 | |
| 600 to 2790 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 34 to 48 | |
| 32 to 57 |
| Strength to Weight: Bending, points | 28 to 35 | |
| 26 to 38 |
| Thermal Diffusivity, mm2/s | 4.6 | |
| 3.3 |
| Thermal Shock Resistance, points | 32 to 45 | |
| 26 to 45 |
Alloy Composition
| Boron (B), % | 0 | |
| 0 to 0.1 |
| Carbon (C), % | 0 to 0.070 | |
| 0 to 0.15 |
| Chromium (Cr), % | 15.5 to 17.7 | |
| 19 to 21 |
| Cobalt (Co), % | 0 | |
| 39 to 41 |
| Copper (Cu), % | 2.5 to 3.2 | |
| 0 |
| Iron (Fe), % | 72.3 to 78.4 | |
| 10 to 20.5 |
| Manganese (Mn), % | 0 to 0.7 | |
| 1.5 to 2.5 |
| Molybdenum (Mo), % | 0 | |
| 6.0 to 8.0 |
| Nickel (Ni), % | 3.6 to 4.6 | |
| 14 to 16 |
| Niobium (Nb), % | 0 to 0.35 | |
| 0 |
| Nitrogen (N), % | 0 to 0.050 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.2 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |