ACI-ASTM CB7Cu-2 Steel vs. EN 1.6570 Steel

Both ACI-ASTM CB7Cu-2 steel and EN 1.6570 steel are iron alloys. They have 80% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB7Cu-2 steel and the bottom bar is EN 1.6570 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 300 to 420
270 to 340
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 5.7 to 11
11 to 17
Fatigue Strength, MPa 420 to 590
500 to 660
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 960 to 1350
910 to 1130
Tensile Strength: Yield (Proof), MPa 760 to 1180
760 to 1060

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Melting Completion (Liquidus), °C 1430
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
40
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 13
3.9
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.6
1.7
Embodied Energy, MJ/kg 38
23
Embodied Water, L/kg 130
56

Common Calculations

PREN (Pitting Resistance) 15
2.5
Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 120
120 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 1510 to 3600
1520 to 3010
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 34 to 48
32 to 40
Strength to Weight: Bending, points 28 to 35
27 to 31
Thermal Diffusivity, mm2/s 4.6
11
Thermal Shock Resistance, points 32 to 45
27 to 33

Alloy Composition

Carbon (C), % 0 to 0.070
0.28 to 0.35
Chromium (Cr), % 14 to 15.5
1.0 to 1.4
Copper (Cu), % 2.5 to 3.2
0
Iron (Fe), % 73.6 to 79
94 to 96.2
Manganese (Mn), % 0 to 0.7
0.6 to 1.0
Molybdenum (Mo), % 0
0.3 to 0.5
Nickel (Ni), % 4.5 to 5.5
1.6 to 2.1
Niobium (Nb), % 0 to 0.35
0
Nitrogen (N), % 0 to 0.050
0
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.015

Comparable Variants