ACI-ASTM CD3MCuN Steel vs. EN 1.0258 Steel

Both ACI-ASTM CD3MCuN steel and EN 1.0258 steel are iron alloys. They have 63% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CD3MCuN steel and the bottom bar is EN 1.0258 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 29
23
Fatigue Strength, MPa 370
200
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 790
490
Tensile Strength: Yield (Proof), MPa 500
290

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
49
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.1
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.9
1.5
Embodied Energy, MJ/kg 54
19
Embodied Water, L/kg 180
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
95
Resilience: Unit (Modulus of Resilience), kJ/m3 620
220
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
17
Strength to Weight: Bending, points 24
18
Thermal Diffusivity, mm2/s 4.1
13
Thermal Shock Resistance, points 22
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.2
Chromium (Cr), % 24 to 26.7
0 to 0.3
Copper (Cu), % 1.4 to 1.9
0 to 0.3
Iron (Fe), % 58.2 to 65.9
96.9 to 100
Manganese (Mn), % 0 to 1.2
0 to 1.4
Molybdenum (Mo), % 2.9 to 3.8
0 to 0.080
Nickel (Ni), % 5.6 to 6.7
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Nitrogen (N), % 0.22 to 0.33
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 1.1
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.020
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020