ACI-ASTM CD4MCuN Steel vs. ASTM A209 Steel

Both ACI-ASTM CD4MCuN steel and ASTM A209 steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CD4MCuN steel and the bottom bar is ASTM A209 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 18
34
Fatigue Strength, MPa 340
180 to 200
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 770
420 to 460
Tensile Strength: Yield (Proof), MPa 550
220 to 250

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1380
1420 to 1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
50
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.1 to 8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 18
2.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.5
1.5
Embodied Energy, MJ/kg 49
20
Embodied Water, L/kg 180
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
120 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 760
130 to 170
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
15 to 16
Strength to Weight: Bending, points 24
16 to 17
Thermal Diffusivity, mm2/s 4.5
13
Thermal Shock Resistance, points 21
12 to 14