ACI-ASTM CE30 Steel vs. EN 1.7357 Steel

Both ACI-ASTM CE30 steel and EN 1.7357 steel are iron alloys. They have 63% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CE30 steel and the bottom bar is EN 1.7357 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11
23
Fatigue Strength, MPa 170
260
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 630
590
Tensile Strength: Yield (Proof), MPa 310
360

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
430
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
41
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 19
2.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.4
1.6
Embodied Energy, MJ/kg 49
21
Embodied Water, L/kg 180
53

Common Calculations

PREN (Pitting Resistance) 28
3.1
Resilience: Ultimate (Unit Rupture Work), MJ/m3 59
120
Resilience: Unit (Modulus of Resilience), kJ/m3 240
340
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 3.6
11
Thermal Shock Resistance, points 13
17

Alloy Composition

Carbon (C), % 0 to 0.3
0.15 to 0.2
Chromium (Cr), % 26 to 30
1.0 to 1.5
Iron (Fe), % 55.1 to 66
96 to 97.9
Manganese (Mn), % 0 to 1.5
0.5 to 1.0
Molybdenum (Mo), % 0
0.45 to 0.65
Nickel (Ni), % 8.0 to 11
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 2.0
0 to 0.6
Sulfur (S), % 0 to 0.040
0 to 0.030