ACI-ASTM CE8MN Steel vs. EN 1.4417 Stainless Steel

Both ACI-ASTM CE8MN steel and EN 1.4417 stainless steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CE8MN steel and the bottom bar is EN 1.4417 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 29
25
Fatigue Strength, MPa 370
380
Poisson's Ratio 0.27
0.27
Shear Modulus, GPa 80
81
Tensile Strength: Ultimate (UTS), MPa 750
730
Tensile Strength: Yield (Proof), MPa 500
550

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 440
450
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
17
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 21
21
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.2
4.1
Embodied Energy, MJ/kg 58
57
Embodied Water, L/kg 180
180

Common Calculations

PREN (Pitting Resistance) 40
41
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
170
Resilience: Unit (Modulus of Resilience), kJ/m3 620
730
Stiffness to Weight: Axial, points 15
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
26
Strength to Weight: Bending, points 23
23
Thermal Diffusivity, mm2/s 4.2
4.6
Thermal Shock Resistance, points 21
20

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.030
Chromium (Cr), % 22.5 to 25.5
24 to 26
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 56 to 66.4
56.7 to 66.9
Manganese (Mn), % 0 to 1.0
0 to 1.5
Molybdenum (Mo), % 3.0 to 4.5
3.0 to 4.0
Nickel (Ni), % 8.0 to 11
6.0 to 8.5
Nitrogen (N), % 0.1 to 0.3
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.020
Tungsten (W), % 0
0 to 1.0