ACI-ASTM CF16F Steel vs. EN 1.4980 Stainless Steel

Both ACI-ASTM CF16F steel and EN 1.4980 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF16F steel and the bottom bar is EN 1.4980 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 50
17
Fatigue Strength, MPa 270
410
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
75
Tensile Strength: Ultimate (UTS), MPa 530
1030
Tensile Strength: Yield (Proof), MPa 280
680

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 420
780
Maximum Temperature: Mechanical, °C 980
920
Melting Completion (Liquidus), °C 1420
1430
Melting Onset (Solidus), °C 1400
1380
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
13
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.1

Otherwise Unclassified Properties

Base Metal Price, % relative 18
26
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.4
6.0
Embodied Energy, MJ/kg 47
87
Embodied Water, L/kg 150
170

Common Calculations

PREN (Pitting Resistance) 22
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
150
Resilience: Unit (Modulus of Resilience), kJ/m3 190
1180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
36
Strength to Weight: Bending, points 19
28
Thermal Diffusivity, mm2/s 4.3
3.5
Thermal Shock Resistance, points 12
22

Alloy Composition

Aluminum (Al), % 0
0 to 0.35
Boron (B), % 0
0.0030 to 0.010
Carbon (C), % 0 to 0.16
0.030 to 0.080
Chromium (Cr), % 18 to 21
13.5 to 16
Iron (Fe), % 61.3 to 72.8
49.2 to 58.5
Manganese (Mn), % 0 to 1.5
1.0 to 2.0
Molybdenum (Mo), % 0 to 1.5
1.0 to 1.5
Nickel (Ni), % 9.0 to 12
24 to 27
Phosphorus (P), % 0 to 0.17
0 to 0.025
Selenium (Se), % 0.2 to 0.35
0
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015
Titanium (Ti), % 0
1.9 to 2.3
Vanadium (V), % 0
0.1 to 0.5