ACI-ASTM CF3MN Steel vs. ACI-ASTM CN3MN Steel

Both ACI-ASTM CF3MN steel and ACI-ASTM CN3MN steel are iron alloys. Both are furnished in the heat treated (HT) condition. They have 80% of their average alloy composition in common.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is ACI-ASTM CN3MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
180
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 39
39
Fatigue Strength, MPa 250
250
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 580
620
Tensile Strength: Yield (Proof), MPa 290
300

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 420
430
Maximum Temperature: Mechanical, °C 1010
1100
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 15
13
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 19
33
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.9
6.2
Embodied Energy, MJ/kg 53
84
Embodied Water, L/kg 160
200

Common Calculations

PREN (Pitting Resistance) 30
46
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
200
Resilience: Unit (Modulus of Resilience), kJ/m3 210
210
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 4.1
3.4
Thermal Shock Resistance, points 13
14

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 17 to 22
20 to 22
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 58.7 to 71.9
41.4 to 50.3
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
6.0 to 7.0
Nickel (Ni), % 9.0 to 13
23.5 to 25.5
Nitrogen (N), % 0.1 to 0.2
0.18 to 0.26
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.010