ACI-ASTM CF3MN Steel vs. AWS E309H

Both ACI-ASTM CF3MN steel and AWS E309H are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is AWS E309H.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 39
34
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 580
620

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1440
1410
Melting Onset (Solidus), °C 1390
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 19
20
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.9
3.7
Embodied Energy, MJ/kg 53
52
Embodied Water, L/kg 160
180

Common Calculations

PREN (Pitting Resistance) 30
25
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
22
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 4.1
4.0
Thermal Shock Resistance, points 13
16

Alloy Composition

Carbon (C), % 0 to 0.030
0.040 to 0.15
Chromium (Cr), % 17 to 22
22 to 25
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 58.7 to 71.9
55.8 to 65.5
Manganese (Mn), % 0 to 1.5
0.5 to 2.5
Molybdenum (Mo), % 2.0 to 3.0
0 to 0.75
Nickel (Ni), % 9.0 to 13
12 to 14
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.030