ACI-ASTM CF3MN Steel vs. EN 1.1165 Cast Steel

Both ACI-ASTM CF3MN steel and EN 1.1165 cast steel are iron alloys. They have 66% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is EN 1.1165 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
11 to 20
Fatigue Strength, MPa 250
200 to 380
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 580
600 to 780
Tensile Strength: Yield (Proof), MPa 290
290 to 620

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1010
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 19
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.9
1.4
Embodied Energy, MJ/kg 53
19
Embodied Water, L/kg 160
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
81 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 210
230 to 1010
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
21 to 28
Strength to Weight: Bending, points 20
20 to 24
Thermal Diffusivity, mm2/s 4.1
14
Thermal Shock Resistance, points 13
19 to 25

Alloy Composition

Carbon (C), % 0 to 0.030
0.25 to 0.32
Chromium (Cr), % 17 to 22
0
Iron (Fe), % 58.7 to 71.9
97.2 to 98.6
Manganese (Mn), % 0 to 1.5
1.2 to 1.8
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 9.0 to 13
0
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.5
0 to 0.6
Sulfur (S), % 0 to 0.040
0 to 0.030