ACI-ASTM CF3MN Steel vs. EN 1.4016 Stainless Steel

Both ACI-ASTM CF3MN steel and EN 1.4016 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is EN 1.4016 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 39
22
Fatigue Strength, MPa 250
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Tensile Strength: Ultimate (UTS), MPa 580
520
Tensile Strength: Yield (Proof), MPa 290
290

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 420
410
Maximum Temperature: Mechanical, °C 1010
870
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
25
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 19
8.5
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.9
2.1
Embodied Energy, MJ/kg 53
29
Embodied Water, L/kg 160
120

Common Calculations

PREN (Pitting Resistance) 30
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
95
Resilience: Unit (Modulus of Resilience), kJ/m3 210
210
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
19
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 4.1
6.7
Thermal Shock Resistance, points 13
19

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 17 to 22
16 to 18
Iron (Fe), % 58.7 to 71.9
79.9 to 84
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 9.0 to 13
0
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015