ACI-ASTM CF3MN Steel vs. EN 1.4568 Stainless Steel

Both ACI-ASTM CF3MN steel and EN 1.4568 stainless steel are iron alloys. They have a moderately high 90% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is EN 1.4568 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 39
2.3 to 21
Fatigue Strength, MPa 250
220 to 670
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
76
Tensile Strength: Ultimate (UTS), MPa 580
830 to 1620
Tensile Strength: Yield (Proof), MPa 290
330 to 1490

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 420
410
Maximum Temperature: Mechanical, °C 1010
890
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 19
13
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.9
2.8
Embodied Energy, MJ/kg 53
40
Embodied Water, L/kg 160
140

Common Calculations

PREN (Pitting Resistance) 30
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
36 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 210
290 to 5710
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
30 to 58
Strength to Weight: Bending, points 20
25 to 40
Thermal Diffusivity, mm2/s 4.1
4.3
Thermal Shock Resistance, points 13
23 to 46

Alloy Composition

Aluminum (Al), % 0
0.7 to 1.5
Carbon (C), % 0 to 0.030
0 to 0.090
Chromium (Cr), % 17 to 22
16 to 18
Iron (Fe), % 58.7 to 71.9
70.9 to 76.8
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 9.0 to 13
6.5 to 7.8
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 0.7
Sulfur (S), % 0 to 0.040
0 to 0.015