ACI-ASTM CF3MN Steel vs. EN 1.4580 Stainless Steel

Both ACI-ASTM CF3MN steel and EN 1.4580 stainless steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is EN 1.4580 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
200
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 39
40
Fatigue Strength, MPa 250
210
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 580
620
Tensile Strength: Yield (Proof), MPa 290
250

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 420
480
Maximum Temperature: Mechanical, °C 1010
950
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 19
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.9
4.3
Embodied Energy, MJ/kg 53
60
Embodied Water, L/kg 160
150

Common Calculations

PREN (Pitting Resistance) 30
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
200
Resilience: Unit (Modulus of Resilience), kJ/m3 210
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
22
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 4.1
4.0
Thermal Shock Resistance, points 13
14

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 17 to 22
16.5 to 18.5
Iron (Fe), % 58.7 to 71.9
61.4 to 71
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
2.0 to 2.5
Nickel (Ni), % 9.0 to 13
10.5 to 13.5
Niobium (Nb), % 0
0 to 1.0
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015