MakeItFrom.com
Menu (ESC)

ACI-ASTM CF3MN Steel vs. EN 1.5682 Steel

Both ACI-ASTM CF3MN steel and EN 1.5682 steel are iron alloys. They have 75% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is EN 1.5682 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
230
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
21
Fatigue Strength, MPa 250
400
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
72
Tensile Strength: Ultimate (UTS), MPa 580
770
Tensile Strength: Yield (Proof), MPa 290
570

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 1010
430
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
8.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
9.8

Otherwise Unclassified Properties

Base Metal Price, % relative 19
7.5
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.9
2.3
Embodied Energy, MJ/kg 53
31
Embodied Water, L/kg 160
63

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
150
Resilience: Unit (Modulus of Resilience), kJ/m3 210
870
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
27
Strength to Weight: Bending, points 20
23
Thermal Shock Resistance, points 13
23

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.13
Chromium (Cr), % 17 to 22
0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 58.7 to 71.9
88.7 to 91.1
Manganese (Mn), % 0 to 1.5
0.3 to 0.8
Molybdenum (Mo), % 2.0 to 3.0
0 to 0.1
Nickel (Ni), % 9.0 to 13
8.5 to 9.5
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.5
0.15 to 0.35
Sulfur (S), % 0 to 0.040
0 to 0.0050
Vanadium (V), % 0
0 to 0.050