ACI-ASTM CF3MN Steel vs. EN 1.7767 Steel

Both ACI-ASTM CF3MN steel and EN 1.7767 steel are iron alloys. They have 70% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is EN 1.7767 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
200 to 210
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
20
Fatigue Strength, MPa 250
320 to 340
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
74
Tensile Strength: Ultimate (UTS), MPa 580
670 to 690
Tensile Strength: Yield (Proof), MPa 290
460 to 500

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1010
480
Melting Completion (Liquidus), °C 1440
1470
Melting Onset (Solidus), °C 1390
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
40
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 19
4.5
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.9
2.4
Embodied Energy, MJ/kg 53
33
Embodied Water, L/kg 160
64

Common Calculations

PREN (Pitting Resistance) 30
6.4
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
120 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 210
570 to 650
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
24
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 4.1
11
Thermal Shock Resistance, points 13
19 to 20

Alloy Composition

Carbon (C), % 0 to 0.030
0.1 to 0.15
Chromium (Cr), % 17 to 22
2.8 to 3.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 58.7 to 71.9
93.8 to 95.8
Manganese (Mn), % 0 to 1.5
0.3 to 0.6
Molybdenum (Mo), % 2.0 to 3.0
0.9 to 1.1
Nickel (Ni), % 9.0 to 13
0 to 0.25
Niobium (Nb), % 0
0 to 0.070
Nitrogen (N), % 0.1 to 0.2
0 to 0.012
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0 to 1.5
0 to 0.15
Sulfur (S), % 0 to 0.040
0 to 0.0050
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0.2 to 0.3