ACI-ASTM CF3MN Steel vs. EN 1.8152 Steel

Both ACI-ASTM CF3MN steel and EN 1.8152 steel are iron alloys. They have 67% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is EN 1.8152 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
200 to 540
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
72
Tensile Strength: Ultimate (UTS), MPa 580
660 to 2010

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Mechanical, °C 1010
410
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
47
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 19
2.2
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.9
1.8
Embodied Energy, MJ/kg 53
25
Embodied Water, L/kg 160
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
24 to 72
Strength to Weight: Bending, points 20
22 to 46
Thermal Diffusivity, mm2/s 4.1
13
Thermal Shock Resistance, points 13
20 to 60

Alloy Composition

Carbon (C), % 0 to 0.030
0.51 to 0.59
Chromium (Cr), % 17 to 22
0.5 to 0.8
Iron (Fe), % 58.7 to 71.9
96 to 97.2
Manganese (Mn), % 0 to 1.5
0.5 to 0.8
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 9.0 to 13
0
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.5
1.2 to 1.6
Sulfur (S), % 0 to 0.040
0 to 0.025
Vanadium (V), % 0
0.1 to 0.2