ACI-ASTM CF3MN Steel vs. N08366 Stainless Steel

Both ACI-ASTM CF3MN steel and N08366 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is N08366 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
180
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 39
34
Fatigue Strength, MPa 250
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 580
590
Tensile Strength: Yield (Proof), MPa 290
240

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 420
430
Maximum Temperature: Mechanical, °C 1010
1100
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
460
Thermal Conductivity, W/m-K 15
13
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 19
33
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.9
6.2
Embodied Energy, MJ/kg 53
84
Embodied Water, L/kg 160
200

Common Calculations

PREN (Pitting Resistance) 30
42
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
160
Resilience: Unit (Modulus of Resilience), kJ/m3 210
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 20
20
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 4.1
3.4
Thermal Shock Resistance, points 13
13

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.035
Chromium (Cr), % 17 to 22
20 to 22
Iron (Fe), % 58.7 to 71.9
42.4 to 50.5
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
6.0 to 7.0
Nickel (Ni), % 9.0 to 13
23.5 to 25.5
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.030