ACI-ASTM CF3MN Steel vs. S31060 Stainless Steel

Both ACI-ASTM CF3MN steel and S31060 stainless steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is S31060 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 39
46
Fatigue Strength, MPa 250
290
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 580
680
Tensile Strength: Yield (Proof), MPa 290
310

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 420
440
Maximum Temperature: Mechanical, °C 1010
1080
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1390
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 19
18
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.9
3.4
Embodied Energy, MJ/kg 53
48
Embodied Water, L/kg 160
170

Common Calculations

PREN (Pitting Resistance) 30
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
260
Resilience: Unit (Modulus of Resilience), kJ/m3 210
250
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
24
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 4.1
4.0
Thermal Shock Resistance, points 13
15

Alloy Composition

Boron (B), % 0
0.0010 to 0.010
Carbon (C), % 0 to 0.030
0.050 to 0.1
Cerium (Ce), % 0
0 to 0.070
Chromium (Cr), % 17 to 22
22 to 24
Iron (Fe), % 58.7 to 71.9
61.4 to 67.8
Lanthanum (La), % 0
0 to 0.070
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 9.0 to 13
10 to 12.5
Nitrogen (N), % 0.1 to 0.2
0.18 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 0.5
Sulfur (S), % 0 to 0.040
0 to 0.030