ACI-ASTM CF3MN Steel vs. Zamak 3

ACI-ASTM CF3MN steel belongs to the iron alloys classification, while Zamak 3 belongs to the zinc alloys. There are 30 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is Zamak 3.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
83
Elastic (Young's, Tensile) Modulus, GPa 200
86
Elongation at Break, % 39
11
Fatigue Strength, MPa 250
48
Poisson's Ratio 0.28
0.25
Shear Modulus, GPa 78
33
Tensile Strength: Ultimate (UTS), MPa 580
280
Tensile Strength: Yield (Proof), MPa 290
210

Thermal Properties

Latent Heat of Fusion, J/g 300
120
Maximum Temperature: Mechanical, °C 1010
95
Melting Completion (Liquidus), °C 1440
390
Melting Onset (Solidus), °C 1390
380
Specific Heat Capacity, J/kg-K 480
410
Thermal Conductivity, W/m-K 15
110
Thermal Expansion, µm/m-K 16
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
27
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
38

Otherwise Unclassified Properties

Base Metal Price, % relative 19
11
Density, g/cm3 7.8
6.4
Embodied Carbon, kg CO2/kg material 3.9
3.0
Embodied Energy, MJ/kg 53
57
Embodied Water, L/kg 160
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
28
Resilience: Unit (Modulus of Resilience), kJ/m3 210
260
Stiffness to Weight: Axial, points 14
7.5
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 20
12
Strength to Weight: Bending, points 20
15
Thermal Diffusivity, mm2/s 4.1
43
Thermal Shock Resistance, points 13
8.6

Alloy Composition

Aluminum (Al), % 0
3.5 to 4.3
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 17 to 22
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 58.7 to 71.9
0 to 0.1
Lead (Pb), % 0
0 to 0.0050
Magnesium (Mg), % 0
0.020 to 0.060
Manganese (Mn), % 0 to 1.5
0
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 9.0 to 13
0 to 0.020
Nitrogen (N), % 0.1 to 0.2
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.5
0 to 0.030
Sulfur (S), % 0 to 0.040
0
Tin (Sn), % 0
0 to 0.0030
Zinc (Zn), % 0
95.3 to 96.5