ACI-ASTM CG6MMN Steel vs. EN 1.5507 Steel

Both ACI-ASTM CG6MMN steel and EN 1.5507 steel are iron alloys. They have 58% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CG6MMN steel and the bottom bar is EN 1.5507 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
140 to 260
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 670
450 to 880

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1080
410
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 17
13

Otherwise Unclassified Properties

Base Metal Price, % relative 22
2.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.8
1.4
Embodied Energy, MJ/kg 68
19
Embodied Water, L/kg 180
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
16 to 31
Strength to Weight: Bending, points 22
17 to 26
Thermal Shock Resistance, points 14
13 to 26

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.080
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.060
0.21 to 0.25
Chromium (Cr), % 20.5 to 23.5
0.25 to 0.35
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 51.9 to 62.1
97.8 to 98.7
Manganese (Mn), % 4.0 to 6.0
0.8 to 1.0
Molybdenum (Mo), % 1.5 to 3.0
0
Nickel (Ni), % 11.5 to 13.5
0
Niobium (Nb), % 0.1 to 0.3
0
Nitrogen (N), % 0.2 to 0.4
0
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0 to 1.0
0 to 0.15
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0.1 to 0.3
0