ACI-ASTM CH20 Steel vs. ACI-ASTM CF3M Steel

Both ACI-ASTM CH20 steel and ACI-ASTM CF3M steel are iron alloys. Both are furnished in the heat treated (HT) condition. They have a moderately high 92% of their average alloy composition in common.

For each property being compared, the top bar is ACI-ASTM CH20 steel and the bottom bar is ACI-ASTM CF3M steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
150
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
55
Fatigue Strength, MPa 290
270
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 610
520
Tensile Strength: Yield (Proof), MPa 350
260

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 440
420
Maximum Temperature: Mechanical, °C 1100
990
Melting Completion (Liquidus), °C 1410
1440
Melting Onset (Solidus), °C 1430
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
16
Thermal Expansion, µm/m-K 15
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.7
3.8
Embodied Energy, MJ/kg 53
53
Embodied Water, L/kg 180
160

Common Calculations

PREN (Pitting Resistance) 25
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
240
Resilience: Unit (Modulus of Resilience), kJ/m3 300
170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
18
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 3.7
4.3
Thermal Shock Resistance, points 15
12

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.030
Chromium (Cr), % 22 to 26
17 to 21
Iron (Fe), % 54.7 to 66
59.9 to 72
Manganese (Mn), % 0 to 1.5
0 to 1.5
Molybdenum (Mo), % 0 to 0.5
2.0 to 3.0
Nickel (Ni), % 12 to 15
9.0 to 13
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 2.0
0 to 1.5
Sulfur (S), % 0 to 0.040
0 to 0.040